Haolic TPU Hot Melt Powder For DTF Transfers
Product Information
|
Brand Name
|
Netural
|
|
Product Name
|
Heat transfer machine adhesive TPU hot melt shaking powder dtf for waterbase dtf ink PET direct transfer film powder printing
|
|
Color
|
White
|
|
Package
|
1kg/5kg in bag
|
|
Composition
|
TPU
|
|
Soften point
|
92±5 ℃
|
|
Application
|
Fabric heat transfer shaking
|
|
Powder size range
|
0-80 um
|
|
Shelf life
|
12 Months
|
Description:(shaking powder dtf)
Dtf hot melt powder features:
1.Polyurethane thermoplastic powder hot melt adhesive.Soft feel and certain resilience, excellent processing.Excellent adhesion to fabric, cotton, blended fabric, TPU, PVC
Dtf hot melt powder features:
1.Polyurethane thermoplastic powder hot melt adhesive.Soft feel and certain resilience, excellent processing.Excellent adhesion to fabric, cotton, blended fabric, TPU, PVC
Guarantee:
1.High quality assurance,3 times QC testing before ex-factory.
2.Responsible and thoughtful after-sale service.
3.100% guarantee and 1:1 replacement for defective goods.
4.Competitive prices,for larger quantity prices are consultable.
5.Fast delivery.
1.High quality assurance,3 times QC testing before ex-factory.
2.Responsible and thoughtful after-sale service.
3.100% guarantee and 1:1 replacement for defective goods.
4.Competitive prices,for larger quantity prices are consultable.
5.Fast delivery.
Advantage:
1) Dark color printing, good matching the materials;
2) Long-term usage, 12 months quality guarantee period；
3) Sample ordering is welcome , More cost-effective for large quantity.
1) Dark color printing, good matching the materials;
2) Long-term usage, 12 months quality guarantee period；
3) Sample ordering is welcome , More cost-effective for large quantity.
Products Description
|
Using Condition
(Reference Only)
|
Temperature
|
120-150℃
|
|
Press
|
1.5-2.5 kg/cm2
|
|
|
Time
|
5-10S
|
|
|
Washing Resistance |
40℃-60℃
|
Excellent
|
|
≥60℃
|
Not recommended
|
Attention:
1.Must be stored in dry unopened package. High temperature and pressure will cause agglomeration. The trays cannot be double-pressed.
2. Bonding temperature and pressure and time relate to the bonding strength of the film to the material. The bonding temperature must be close to the temperature set by the machine, the pressure must be uniform, and the mold and press rolls must be flat.
3. The bonding conditions used will vary between machines and materials. The conditions indicated here are only basic. The most ideal bonding conditions should be established by manufacturing for the specific application.
3. The bonding conditions used will vary between machines and materials. The conditions indicated here are only basic. The most ideal bonding conditions should be established by manufacturing for the specific application.
Haolic TPU Hot Melt Powder For DTF Transfers